Sign In | Join Free | My
Changzhou Junhe Technology Stock Co.,Ltd
Walk at the forefront of technology, to create a ceneration of famous brand!
Home > Dacromet Coating >

Low Friction Dacromet Coating Friction Coefficient Of Small 0.12-0.18 PH 3.8-5.2

Changzhou Junhe Technology Stock Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Changzhou Junhe Technology Stock Co.,Ltd
City: Changzhou
Province/State: Jiangsu
Country/Region: China
Tel: 86-519-85922787
Contact Person:
Mrs June

Low Friction Dacromet Coating Friction Coefficient Of Small 0.12-0.18 PH 3.8-5.2

Brand Name : JUNHE
Model Number : JH-9510
Certification : ISO9001 TS16949
Place of Origin : Changzhou in china
MOQ : 100 Kilograms
Price : Negotiable
Supply Ability : 2 Tons per Day
Delivery Time : Ten days after receipt of advance payment
Packaging Details : Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A
Coating method : Dip spin & Spray
Color : Silver
PH : 3.8-5.2
Specific gravity : 1.33±0.05 (spray coating) 1.33±0.05(dip-spin coating)
Viscosity : 20~60seconds(spray coating) 60-80seconds(dip-spin coating)
Operating temperature : 20±2℃
Contact Now
Low friction Dacromet Coating friction coefficient of small 0.12-0.18 PH 3.8-5.2
Product Description

JH-9510 is made up of three packs: A,B and C;

Pack A: It is silver gray slurry that mainly chemically combined with super fine flake Zn, super fine flake Al and organic additive.

Pack B: It is water solution that mainly combined with corrosion protecion additive, particular regulator water solution etc.

Pack C: It is the tackifier of the coating which mainly made up of cellulose white or yellowish powder.

Performance characteristics:

The film is silver white, good surface finish, high corrosion resistance, and then good friction coefficient of small 0.12-0.18

Coating Process:

1. Mix Ratio

Pack A: Pack B: Pack C=1:1: X(according to different viscosity demand )

2. Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B.

3. Add B to the stirring A slowly.

4. Stir the mixture about 1~2 hours after B added, then add C. C should be powdered if lump exist.(The barrel temperature should not be lower than 30℃, otherwise C will not be dissolved sufficiently .)Then stir 12 hours alowly and continuously.

5. The coating should be filtrated by 100 mesh stainless steel screen before pouring into dip barrel.

6. Temperature control device should be equipped with dip barrel to keep the temperature of coating at 22±2℃.(If temp. is too high, the paint is liable to deteriorate, and viscosity will be effected.) The coating should be stirred circularly to keep evenly dispersed.

7. Test Specific gravity,PH,Temperature,Viscosity of coating every 8 hours if operate continuously.

Technical data:

2Coating methodDip Spin & Spraying
4Specific gravity1.33±0.05 (spray coating) 1.33±0.05(dip-spin coating)
5Viscosity20~60seconds(spray coating) 60-80seconds(dip-spin coating)
6Operating temperature20±2℃

Mix Diagram:

Coating Process:


Other chemicals such as any kinds of acid, alkali salt can not be mixed into coating, for these can activate Zn & Al plate to aging the coating.

Avoid irradiation of sunshine and ultraviolet ray for long time when operating, otherwise it will accelerate aging or polymerization of the coating .

It is very important to control the temperature of coating. If the temperature of coating changes when operating, it will effect the viscosity, then effec the coating quatity on workpiece. So the relations among temperature,viscosity and spinning process shoud be controlled well when coating.

The viscosity will be different if coating method is different. Choose low data if spray coating,and choose high data if dip spin coating.

Product Tags:

Dacromet Coated Bolts


Zinc Aluminium Flake Coating

China Customized Inflatable Bumper Ball Game Bubble Adult Grass CE supplier

Low Friction Dacromet Coating Friction Coefficient Of Small 0.12-0.18 PH 3.8-5.2 Images

Inquiry Cart 0
Send your message to this supplier
Enter your email please.
To: Changzhou Junhe Technology Stock Co.,Ltd
Characters Remaining: (0/3000)