JH-9088 High Corrosion Resistance Nanometer Alloy Coating Density
1 Product Information
According to the galvanized coating have poor corrosion resistance
and defect of acid and alkali resistant,our companyI developed
JH-9088 high corrosion nano alloy coatings.It can improve the
corrosion performance of the coating,make the salt spray time
increased to more than 1000 hours, but also increase the hardness,
acid and alkali-resistant on the coating surface, and the surface
color can be diversified.
2 Composition/information on ingredients
The basic materials of this product is nano-alloy powder,
toughening agents, film formers, organic solvents and color paste,
adding other additives mixed.
3 Performance Characteristics
This product can be use by dipping and spraying ways to treat on
galvanized parts, parts surface treated uniformly, no blind spots.
The treated parts,anti-corrosion ablity is ten times exceed
galvanized workpieces, salt spray time increased to more than 1000
hours. And have excellent heat-resistant and antiacid,
anti-alkali,anti-salt and other properties, its smooth surface,
high hardness, anti-scratch, color can meet the needs of the
4 Market Application
This product is suitable for long-term corrosion protection for
outdoor galvanized parts. Such as railway fasteners, bridges,
buildings, power communications fasteners, etc.
5 Construction Method and Attention
5.1 This product can use spraying and dipping ways for coating.
5.2 Fully stirring before use, should use special diluent to adjust
5.3 Add centrifugal procedure for dipping process.
5.4 Cleaning appliance, use alcohol or ether organic solvents
Packing:Steel drum,Net weight:20kg/drum(can also according to
Storage:Tightly closed,below 40℃,keep in indoor places, without
Transportation:Should prevent rain, sun exposure, and shall comply
with the relevant provisions of the transport sector.
7 Coating process
7.1 Process flow
Galvanized parts dipping Spraying Pre-curing,Curing Inspection
7.2 Process parameters
Dipping: Room temperature,density:30-45s.
Centrifuge dripping: 210-270/min,30-60s
Spraying:: Room temperature,density:25-35s.
7.3 Curing Condition
Pre-curing:Temperature:80-150℃,10-15min,choose whether pre-curing
depend on the thickness of the workpiece.
Curing:Temperature:200-220℃,20-30min, box-type furnace or channel
devices both ok.
8 Technical Data
|1||Apperance||Silver Coating liquid|
|2||Density||0.9-1.2g/ml||50ml hydrometer jar|
|4||Diluent||Use diluent djust to the coating viscosity||JH-9088B Diluent|
9 Coating Liquid Viscosity and The Amount of Diluent Synopsis
|NO||Coating Liquid (g)||Diluent (g)||Density (s)|